MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
卷 527, 期 6, 页码 1501-1509出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2009.10.016
关键词
Sliding wear; Aluminum alloy composite; Fly ash; High temperature
类别
资金
- Department of Technical Education (Govt. of Andhra Pradesh)
- All India Council for Technical Education, New Delhi
- World Bank
The effect of fly ash particulate on high temperature dry sliding wear resistance of AA6061, developed by powder metallurgy and hot extrusion, was studied. The dry sliding wear behavior of the prepared composite was investigated by using pin-on-disc method at an applied load of 14.6N for various temperatures (100, 200 and 300 degrees C). The study at room temperature was also carried out for comparison purpose. The results had shown transition from mild-to-severe wear for unreinforced alloy in the temperature range of 200-300 degrees C. With the addition of fly ash to AA6061, the mild-to-severe wear transition was not noticed even up to 300 degrees C. This behavior was attributable to the formation of protective transfer layers of comminuted reinforcing particulates and transferred steel debris from slider counterpaces. The absence of severe wear phenomena in this composite was due to the particulate hardening of subsurface layer in the temperature range investigated. (C) 2009 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据