Composite; Stir-casting; YAl2 intermetallics; Microstructure; Mechanical property
类别
资金
- Ministry Education of People's Republic Foundation of China [20070006020]
- Beijing Nova Program [2007B016]
MgLiAl matrix composite reinforced with YAl2 intermetallics particles were developed by stir-casting. Microstructure features of the YAl2/MgLiAl composite were investigated. The results show that a good particle distribution and interfacial bonding are obtained. There are no reaction products at particle/matrix interface. YAl(2)p/Mg-Li-Al composites have excellent comprehensive mechanical properties. The tensile strength and yield strength are significantly improved by the addition of YAl2 particulates, while a good ductility property is kept. At room temperature, tensile strength, yield strength and elongation of 20%YAl(2)p/Mg-Li-Al composite are 225, 161.4 MPa and 9% respectively. The addition of YAl2 particulates improves the deformation resistance at high temperature of the magnesium-lithium based composites, which makes the composites have good mechanical properties at high temperature. At 180 degrees C, the tensile strength and yield strength of 20%YAl2 p/Mg-Li-Al composite are 78, 57 MPa respectively, and increase over past 100% and 200% than that of matrix alloy. (C) 2009 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据