MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
卷 517, 期 1-2, 页码 354-360出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2009.04.029
关键词
AZ91 alloy; Pre-aging treatment; Hot compression; Microstructure; Mechanical properties
类别
资金
- New Energy and Industrial Technology Development Organization (NEDO), Japan
Hot compression tests were performed on the as-cast and aged Mg-9Al-1Zn (AZ91) alloy specimens at temperature of 300 degrees C to investigate the influence of pre-aging treatment on microstructure and mechanical properties of the hot compressed AZ91 alloy. The results show that the pre-aging treatment can be effective in increasing the precipitation number Of Mg17Al12 phase and enlarging the discontinuous precipitates area, in which the dynamic recrystallization (DRX) occurs with discontinuous precipitates pinning at the newly-DRXed grain boundaries, leading the DRX ratio and (0001) (11 (2) over bar0) basal slip Schmid factor of the compressed specimens being increased. Both the ultimate tensile strength (UTS) and elongation to failure are higher in the age-compressed specimens. After compression at 300 degrees C and a strain rate of 0.2 s(-1) with a compression ratio of 50%, UTS of the age-compressed specimen (336 MPa) is 44 MPa higher than that of cast-compressed specimen (292 MPa), and elongation to failure of the age-compressed specimen (9.8%) is three times as that of cast-compressed specimen (3.3%). (C) 2009 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据