nickel-base superalloy; low cycle fatigue; cyclic deformation; cyclic stress response
Total strain-controlled low cycle fatigue (LCF) tests were performed at a temperature range from 700 to 900 degrees C in ambient air condition on a directionally solidified Ni-base superalloy DZ951. The fatigue life of DZ951 alloy does not monotonously decrease with increasing temperature, but exhibits a strong dependence on the total strain range. The dislocation characteristics and failed Surface observation were evaluated through transmission electron microscopy and scanning electron microscopy. The alloy exhibits cyclic hardening, softening or cyclic stability as a whole. which is dependent on the testing temperature and total strain range. At 700 degrees C, the cyclic plastic deformation process is the main cause of fatigue failure. At 900 degrees C, the failure mostly results front combined fatigue and creep damage under total strain range from 0.6 to 1.2% and the reduction in fatigue life can be taken as the cause of oxidation, creep and cyclic plastic deformation under total strain range of 0.5%. (C) 2007 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据