MATERIALS RESEARCH BULLETIN
卷 46, 期 6, 页码 796-800出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.materresbull.2011.02.041
关键词
Lithium-ion battery; Spinel; Spray pyrolysis; Powder; Lithium titanate
资金
- Japan Science and Technology Agency (JST)
- Project Research Center in the School of Engineering from the University of Fukui
A composite powder of Li4Ti5O12 and carbon (LTO/C) was synthesized by spray pyrolysis using an aqueous solution of Li and Ti with an organic acid. As-prepared LTO/C particles had spherical morphology and nonaggregation characteristics. They also had a particle size of approximately 1 mu m with a broad size distribution. As-prepared LTO/C powders were crystallized to have a spinel structure. The addition of lactic acid was most effective for improving the electrochemical properties of LTO/C. The rechargeable capacity of the LTO/C anode obtained from lactic acid was 164 mAh/g at 1 C. The retention was 96% after 100 cycles at 1 C. The rechargeable capacity of the LTO/C anode decreased with an increasing charge rate. The rechargeable capacity of LTO/C obtained from lactic acid was 150 mAh/g at 10 C. The cycle performance of the LTO/C anode obtained from lactic acid also had a high stability at 50 degrees C. (C) 2011 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据