Nanostructured Zn and ZnO nanowire thin films for mechanical and self-cleaning applications

Nanostructured Zn metal films were deposited by thermal evaporation, on borosilicate glass, Quartz, sapphire, lanthanum aluminate and yttria stabilized zirconia substrates. The as-deposited films are nanocrystalline and show a morphology that consists of triangular nanosheets. The films are hydrophobic with contact angles between 102 degrees and 120 degrees with hardness and Young's modulus between 0.15-0.8 GPa and 18-300 GPa, respectively. Thermal annealing of the films at 500 degrees C results only in partial oxidation of Zn to ZnO, which indicates good oxidation resistance. Annealing also causes transformation of the Zn nanosheets into ZnO nanowires that are polycrystalline in nature. The ZnO nanowires are superhydrophobic with contact angles between 159 degrees and 162 degrees contact angle hysteresis between 5 degrees and 10 degrees and exhibit a reversible superhydrophobic-hydrophilic transition under UV irradiation. The nanowires are much softer than the as-deposited Zn metal films, with hardness between 0.02 and 0.4 GPa and Young's modulus between 3 and 35 GPa. The current study thus demonstrates a simple process for fabrication of nanostructured Zn metal films followed by a one-step transformation to nanowires with properties that will be very attractive for mechanical and self-cleaning applications. (C) 2015 Elsevier B.V. All rights reserved.