APPLIED SURFACE SCIENCE
卷 333, 期 -, 页码 207-213出版社
ELSEVIER
DOI: 10.1016/j.apsusc.2015.02.020
关键词
Carbon nanowalls; Oxygen plasma; Atom surface recombination; Loss coefficient
类别
资金
- Slovenian Research Agency [RPROJ-2014-I-365]
- Ministry of National Education CNCS - UEFISCDI [PN-II-ID-PCE-2012-4-0629]
Extremely high values of atomic oxygen loss coefficient on carbon nanowall (CNW) surface are reported. CNW layers consisting of interconnected individual nanostructures with average length of 1.1 mu m, average thickness of 66 nm and surface density of 3 CNW/mu m(2) were prepared by plasma jet enhanced chemical-vapor deposition using C2H2/H-2/Ar gas mixtures. The samples were characterized by scanning electron microscopy (SEM), atomic force microscopy (AFM), transmission electron microscopy (TEM), Raman spectrometry (RS) as well as X-ray photoelectron spectroscopy (XPS). The surface loss coefficient was measured at room temperature in a flowing afterglow at different densities of oxygen atoms supplied from inductively coupled radiofrequency O-2 plasma. The RF generator operated at 13.56 MHz and different nominal powers up to 900 W corresponding to different O-atom density in the afterglow up to 1.3 x 10(21) m(-3). CNW and several different samples of known coefficients for heterogeneous surface recombination of neutral oxygen atoms have been placed separately in the afterglow chamber and the O-atom density in their vicinity was measured with calibrated catalytic probes. Comparison of measured results allowed for determination of the loss coefficient for CNWs and the obtained value of 0.59 +/- 0.03 makes this material an extremely effective sink for O-atoms. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据