Response surface methodology (RSM) coupled with the central composite design (CCD) was used to optimize the mechanical properties of calcium phosphate cement/multi-walled carbon nanotubes/bovine serum albumin (CPC/MWCNTs/BSA) composites. In this study. CPC composites were reinforced by multi-walled carbon nanotubes (MWCNTs) and bovine serum albumin (BSA) in order to induce high mechanical properties in the CPC/MWCNTs/BSA system. The effect of various process parameters on the compressive strength of CPC/MWCNTs/BSA composites was studied using design of experiments (DOE). The process parameters studied were: wt.% of MWCNTs (0.2-0.5 wt.%), wt.% of BSA (5-15 wt.%) and type of MWCNTs (e.g. as-pristine MWCNT (MWCNT-AP), hydroxyl group functionalized MWCNT (MWCNT-OH) and carboxyl group functionalized MWCNT (MWCNT-COOH)). Based on the CCD, a quadratic model was obtained to correlate the process parameters to the compressive strength of CPC/MWCNTs/BSA composites. From the analysis of variance (ANOVA), the most significant factor affected on the experimental design response was identified. The predicted compressive strength after process optimization was found to agree well with the experimental value. The results revealed that at 0.5 wt.% of MWCNT-OH and 15 wt.% of BSA, the highest compressive strength of 14 MPa was obtained. (C) 2011 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据