Effects of trace Er addition on the microstructure and mechanical properties of Mg-Zn-Zr alloy

The effects of trace Er addition on the microstructure in Mg-9Zn-0.6Zr alloy during casting, homogenization, pre-heating, and hot extrusion processes were examined. The mechanical properties of alloys with and without Er were compared. The results showed that Er exhibited a lower solubility in solid magnesium and formed thermally stable Er- and Zn-bearing compounds. The Er-bearing alloy exhibited a considerably improved deformability, as well as a fine and uniform microstructure. Moreover, dynamic precipitation of fine MgZn(2) particles with a modified spherical morphology occurred during hot extrusion, resulting in a tensile yield strength of 313 MPa and a high elongation to failure value of 22%. Further aging of the Er-bearing alloy led to an increment of another 30 MPa in yield strength. In addition, Er markedly increased the thermal stability of the alloy structure. (C) 2010 Elsevier Ltd. All rights reserved.