From Hydrophobic to Superhydrophobic and Superhydrophilic Siloxanes by Thermal Treatment

The cross-influence effects of treatment temperature and time on the wettability of a siloxane elastomer is investigated in detail, through static and tilt contact angle measurements. The material is heated at 400, 500, 600, 650, 700, and 800 degrees C for various periods, ranging from 1 to 300 s. The siloxane surface is subjected to multiple wettability transitions with treatment time: from intrinsic hydrophobicity to superhydrophobicity (and water repellency) and then through intermediate stages (hydrophobicity and hydrophilicity) to superhydrophilicity. For the time scale used herein (1300 s), this scenario is recorded for treatment at 650, 700, and 800 degrees C. For treatment at lower temperatures (400, 500, and 600 degrees C) only the first transition, from intrinsic hydrophobicity to superhydrophobicity, is recorded. Scanning electron microscopy, micro-Fourier transform infrared (micro-FTIR), and micro-Raman spectroscopies are employed to correlate the aforementioned wettability transitions with structural and chemical changes of the siloxane surface, developed during thermal treatment. It is shown that the first transition from intrinsic hydrophobicity to superhydrophobicity is accompanied by a severe surface-structure evolution that increases surface roughness. Once superhydrophobicity is achieved, the surface structure reaches a saturation point and it is not subjected to any other change with further thermal treatment. FTIR spectroscopy shows that the intensity of the OH/CH peaks increases/decreases with treatment time, and Raman measurements show that the CSiC vibrations gradually disappear with treatment time. The evaporation of a droplet resting on a superhydrophobic, water-repellent siloxane surface, which was produced after appropriate thermal treatment, is monitored. It is shown that droplet evaporation initially follows the constant contact area mode. At later evaporation stages, a transition to the constant contact angle mode is recorded. Finally, it is demonstrated that the superhydrophobic and water-repellent siloxane surfaces exhibit self-cleaning properties, good durability, and furthermore do not practically affect the optical transparency of glass substrates.