Microstructural Characteristics of Y2O3-MgO Composite Coatings Deposited by Suspension Plasma Spray

Dense composite Y2O3-MgO coatings have been deposited by suspension plasma spray. Ethanol-based suspensions of powders synthesized by thermal decomposition of precursor solutions containing yttrium nitrate (Y[n]) and magnesium nitrate (Mg[n]) or magnesium acetate (Mg[a]) were selected as the feedstock; this gave powders with both phases in each particle, to inhibit phase segregation during solvent evaporation. The influence of powder characteristics on the microstructures of the coatings was investigated. The Y[n]Mg[a] suspension was more stable, with a better dispersion of the component phases than the Y[n]Mg[n] suspension. The coatings deposited using each suspension type exhibited lamellar structures comprising Y2O3 and MgO phases in wavy alternating streaks, with unmelted/semi-melted particles entrapped in the lamellae; this indicates that phase segregation still occurred in the molten state. Eutectic structures were formed in the coating generated using the Y[n]Mg[a] suspension, resulting from improved mixing of the component phases in the suspension powder.