卷 34, 期 3, 页码 633-639出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2013.10.012
关键词
Radiation tolerance; Titanium nitride; Vacancy defect; Self-heal
资金
- National Natural Science Foundation of China [91026008, 11175228, 11205229]
- State Key Laboratory of High Performance Ceramics and Superfine Microstructures of Shanghai Institute of Ceramics
TiN and TiN0.7 were irradiated using a 100 keV Ar-ion beam at 600 degrees C to target doses of 3 x 10(17) ions cm(-2). SRIM estimation, GIXRD and fluorescence analysis have been performed to evaluate the effect of pre-existing vacancy defect on the radiation tolerance. The lattice parameter of TiN increased after irradiation due to interstitial atoms and vacancies in as-irradiated TiN. In contrary, the lattice parameter decreased for as-irradiated TiN0.7, which indicates that the nitrogen atom vacancies in TiN0.7 acted as sinks for displacement atoms generated by irradiation to limit interstitial atoms existing. The intensity of peaks in fluorescence spectrum of as-irradiated TiN was higher than that of as-irradiated TiN0.7. That atiributed to the presence of color centers formed by Frenkel defects in as-irradiated TiN. All of the results indicate that introducing vacancy defect in materials would offer capability to realize self-heal of irradiation damage. (C) 2013 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据