JOURNAL OF REINFORCED PLASTICS AND COMPOSITES
卷 30, 期 13, 页码 1097-1106出版社
SAGE PUBLICATIONS LTD
DOI: 10.1177/0731684411416532
关键词
thin-ply laminates; CFRP; impact damage; transverse crack; damage localization
资金
- Organization for Small & Medium Enterprises and Regional Innovation, Japan (SMRJ)
In this article, the effects of ply thickness on the impact damage mechanisms in CFRP laminates are discussed based on the experimental observations. Quasi-isotropic CFRP laminates were manufactured using 38 mm thick thin-ply prepregs. Impact damage inside the laminates was evaluated by using ultrasonic scanning and sectional fractography. Compression after impact strength was also evaluated. Thin-ply laminates showed 23% higher strength than standard-ply laminates. Transverse cracks decreased drastically in thin-ply laminates, and localized delamination was largely extended. Based on the discussions in our previous study and the literature, the specific ply thickness without drastic crack propagation appears to be less than or equal to 40 mu m. Therefore, the thin laminates showed few and localized transverse cracks and delamination was largely propagated in the midplane.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据