期刊
JOURNAL OF REINFORCED PLASTICS AND COMPOSITES
卷 29, 期 3, 页码 466-476出版社
SAGE PUBLICATIONS LTD
DOI: 10.1177/0731684408100699
关键词
polypropylene; composites; degradable fibers; mechanical properties; compression molding; interfacial properties
Polypropylene (PP) matrix synthetic phosphate based degradable fiber reinforced unidirectional composites (10% fiber by weight) were fabricated by compression molding. Tensile strength (TS), tensile modulus (TM), elongation at break (%), bending strength (BS), bending modulus (BM), and impact strength (IS) were found to be 38 MPa, 1.5 GPa, 12%, 44 MPa, 4.9 GPa, and 7.58 kJ/m(2) respectively. Degradation tests of the fibers and composites were performed for six months in aqueous medium at room temperature (25 degrees C). After six months, the mechanical properties of the composites retained almost 80% of their original properties. The interfacial shear strength (IFSS) of the composites were also measured by single fiber fragmentation test (SFFT). The IFSS of the composite system was found 5.9MPa that indicated good fiber matrix adhesion.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据