期刊
JOURNAL OF RARE EARTHS
卷 32, 期 5, 页码 451-457出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/S1002-0721(14)60093-4
关键词
AZ31 magnesium alloy; Nd; microstructure; mechanical properties; rare earths
资金
- Liaoning BaiQianWan Talents Program [2011921065]
The effects of precipitates on grain size and mechanical properties of as-cast AZ31-x%Nd magnesium alloy were investigated, and the affecting mechanism was also discussed. The results indicated that Al2Nd phase, Al11Nd3 phase and a few Al-Mn-Nd-Fe phase were formed when adding 0.38 wt.%-1.46 wt.% Nd into AZ31 melt, coarse Al2Nd transformed into Al11Nd3 gradually with the increasing of Nd content. Due to structure and size transformation and content increasing of Al-Nd phase, the grain size of AZ31-x%Nd alloy increased firstly, and then decreased with the increment of Nd content. After reaching a minimum value, once again it rose up, provided that Nd content was further increased. The tensile property reached its optimal value when the adding amount of Nd content was 1.05 wt.%, however, adding excessive amount of Nd deteriorated both ultimate strength and elongation of AZ31 alloy.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据