For the first time, Cu(NO3)(2)center dot xH(2)O (x < 2.5) is investigated as a new lithium storage anode material for lithium-ion batteries. The impressive characteristic of Cu(NO3)(2)center dot xH(2)O(x <= 2.5)/Li cell is the high initial discharge capacity reaching to around 2200 mAh g(-1). To make a comparison, Cu(NO3)(2)center dot 2.5H(2)O electrodes are used as raw materials and heat-treated at 80, 120 and 160 degrees C. Among all the three samples, Cu(NO3)(2)center dot xH(2)O (x < 2.5) obtained at 160 degrees C shows the highest reversible capacity of 597.6 mAh g(-1) and the best cycling stability after 30 cycles. The difference in electrochemical behaviors is attributed to the variation of surface morphology, crystal water and particles size after heat-treatment at different temperatures. Besides, the thermal reaction results also show that Cu(NO3)(2)center dot xH(2)O (x < 2.5) obtained at 160 degrees C has the highest thermal stability among all the three samples after repeated cycles. The present findings can provide the fact that Cu(NO3)(2)center dot xH(2)O (<= 2.5) may be a promising anode material for lithiumion batteries. (C) 2013 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据