(Sm1-xCax)(2)Zr2O7-x; Pyrochlore; Electrical conductivity; Impedance spectroscopy
资金
- Program of Excellent Teams in Harbin institute of Technology (HIT)
(SM1-xCax)(2)Zr2O7-x, (0 <= x <= 0.100) ceramics were prepared by a solid state reaction process at 1973 K for 10h in air, and were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). (SM1-xCax)(2)Zr2O7-x (0 <= x <= 0.025) ceramics have a single phase of pyrochlore-type structure; however (Sm1-x,Ca-x)(2)Zr2O7-x (0.050 <= x <= 0.100) consist of pyrochlore phase and a small amount of perovskite-like CaZrO3. The electrical conductivity of (Sm1-xCax)(2)Zr2O7-x ceramics was investigated by complex impedance spectroscopy over a frequency range of 0.1 Hz to 20 MHz in the temperature range of 573-873 K. The measured electrical conductivity obeys the Arrhenius relation. Both the activation energy and pre-exponential factor for grain conductivity increase with increasing the CaO content; however, electrical conductivity of (Sm1-xCax)(2)Zr2O7-x decreases with increasing the CaO content, which is due to the increase in structural disordering at 0 <= x <= 0.025 and the presence of the poorly conducting CaZrO3 phase at 0.050 <= x <= 0.100, respectively. (C) 2009 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据