JOURNAL OF POWER SOURCES
卷 189, 期 1, 页码 445-448出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jpowsour.2008.12.124
关键词
LiFePO4; Lithium ion cell; Capacity degradation; Impurity; Iron deposition
The physical properties and electrochemical performance of two kinds of commercialized LiFePO4 (hereafter abbreviated as UP) were analyzed. And the cycle stability of the two kinds of material in the 18,650 type lithium ion cells was measured at different charge cut-off voltage (3.65.3.8,4.0 and 4.2V). The two kinds of material showed remarkable difference. One has good cycle stability but another encounters serious failure problem at high charge cut-off voltage (4.2V). Results showed that the impurities containing iron atom in the raw material and formed during the charge-discharge cycles are the main reasons of the failure mechanism. The impurities were reduced on the graphite surface and iron dendrite formed gradually, which may penetrate through the separator and results in the inner short circuit of the cells. (C) 2009 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据