JOURNAL OF NUCLEAR MATERIALS
卷 417, 期 1-3, 页码 270-273出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jnucmat.2011.01.067
关键词
-
The radiation-hardening of oxide dispersion strengthened (ODS) alloys was examined using ion irradiation and nano-indentation. In this work, three ODS steels were irradiated in the TIARA facility at JAEA with 10.5 MeV Fe(3+) ions up to a dose of 20 dpa at 250 and 380 degrees C. Micro-hardness measurements were carried out on the ion-irradiated specimens with ultra-low load indention. Micro-structures were investigated by transmission electron microscopy (TEM) to examine the contribution of various types of defects to the radiation-hardening. All three steels showed increases in the hardness after the ion irradiation, and F82H-ODS showed the lowest radiation-hardening, which suggests that F82H-ODS has the better radiation resistance. Small amounts of particle dissolution was also confirmed in all of the steels after the irradiation. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据