JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY
卷 12, 期 4, 页码 3669-3672出版社
AMER SCIENTIFIC PUBLISHERS
DOI: 10.1166/jnn.2012.5631
关键词
ZnO Thin Film; Texture; Light Trapping; Solar Cell
类别
资金
- KIST [2E22152]
The effect of precursor ratio (H2O/DEZ) on the texture orientation, surface morphology, optical transparency and electrical resistivity of ZnO thin films deposited by MOCVD was investigated. Deposition temperature and pressure were fixed at 120 degrees C and 0.67 torr, respectively. The precursor ratio was varied between 0.1 and 4. It was found that the texture orientation changed from < 0002 > to < 1120 > with increase of the precursor ratio. < 1120 > textured film shows well facetted tetrapod like rough surface morphology, which scatters the incident light very effectively. The electrical resistivity was in the range of about 0.1 Omega cm in the undoped state, which was found to decrease with increase of the film thickness and decrease of the precursor ratio.