期刊
JOURNAL OF MOLECULAR STRUCTURE
卷 1075, 期 -, 页码 154-158出版社
ELSEVIER
DOI: 10.1016/j.molstruc.2014.07.003
关键词
Phosphomolybdic acid; Polyvinyl pyrrolidone; SiO2 doping; Hybrid films; Photochromism
资金
- National Natural Science Foundation of China [61340048]
- Specialized Research Fund for the Doctoral Program of Higher Education of China [20110041120001]
- Industrial Technology Research and Development projects in Jilin province [2013C044]
New hybrid films were synthesized by SiO2 doping into phosphomolybdic acid (PMoA)/polyvinyl pyrrolidone (PVPd) composite system, and the effect of SiO2 doping on microstructure and photochromic properties was studied via atomic force microscope (AFM), Fourier transform infrared spectroscopy (FT-IR), ultraviolet-visible spectra (UV-vis) and X-ray photoelectron spectroscopy (XPS). The hybrid film surface with dome projection changed rough from smooth after SiO2 doping. The vibrational spectra of FT-IR verified that component of the heteropolyacids and the polymer did not changed, the vibration bands were expanded and had shifted by a few cm(-1), and changed interaction between the acid and the polymer after SiO2 doping. The hybrid film exhibited a good photochromic property, which changed from colorless to blue under UV irradiation. The color change intensity of SiO2/PMoA/PVPd film was 1.48 times stronger than that of PMoA/PVPd under the same condition. XPS results indicated that the amount of PMoA in photo-reductive reaction was increased after SiO2 doping. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据