JOURNAL OF MEMBRANE SCIENCE
卷 378, 期 1-2, 页码 512-519出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.memsci.2011.05.040
关键词
Sulfonated poly(arylene ether); Crosslinking; Reverse osmosis (RO); Chlorine resistance membrane
资金
- Ministry of Land, Transport and Maritime Affairs [07seaHEROB02-03-01]
- World Class University (WCU) [R31-20008-000-10026-0]
Crosslinked (C-ESFx-BP) and non-crosslinked (N-ESFx-BP) sulfonated poly(arylene ether) (SPAE) membranes containing high fluorine contents were prepared as a function of the degree of sulfonation (DS) and evaluated for use as a highly potential chlorine-resistant reverse osmosis (RO) membrane. C-ESFx-BP membranes were obtained by covalent crosslinking among ethynyl end groups of the polymer chains via thermal curing. Both C-ESFx-BP and N-ESFx-BP membranes show the increase in NaCl rejection with decreasing DS, while water permeability declines due to the decrease of hydrophilicity. In particular, C-ESF70-BP membrane showed excellent salt (NaCl) rejection up to 98.4% compared with that of N-ESF70-BP membrane of 90.3% but showed slightly lower water permeability of 0.6 L mu m/m(2) h bar than that of 0.8 L mu m/m(2) h bar for N-ESF70-BP. Moreover, these C-ESFx-BP and N-ESFx-BP membranes displayed the long-term stability longer than 30 days during the operation condition under high acidic chlorine concentration of NaOCl 4000 ppm unlike commercial PA membranes which are unstable under the chlorine treatment. The stability comparison between them were observed by ATR-IR, retention ratio of molecular weight (RRMW), contact angle and X-ray photoelectron spectroscopy (XPS). (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据