期刊
JOURNAL OF MEMBRANE SCIENCE
卷 319, 期 1-2, 页码 126-132出版社
ELSEVIER
DOI: 10.1016/j.memsci.2008.03.026
关键词
membrane; ceramic-supported polymer; polyimide; pervaporation; dehydration
Ceramic-supported polymer (CSP) membranes were prepared based on Torlon, P84, and Matrimid. The dehydration performance of these membranes was determined by pervaporation of n-butanol/water mixtures (95/5 wt%) at 95 degrees C. Based on their performance P84 was selected for further testing. P84 membranes showed excellent separation performance in dehydration of n-butanol for at least 300 days. Different curing temperatures in the range of 70-300 degrees C were used. The most significant flux difference was seen for a P84 membrane cured at 300 degrees C, compared to the lower temperatures. The separation performance of a P84 CSP membrane at 150 degrees C showed water fluxes in the range of 1-6 kg/m(2) h and separation factors of at least 360. The membrane life-time in n-butanol/water mixtures ranges from 80 to 140 days at 150 degrees C. No clear relation between curing temperature and membrane stability could be derived. Reasonable separation performance of a P84 CSP membrane in an ethanol/water mixture was demonstrated. Stable performance at 150 degrees C was observed for the dehydration of t-butanol up to at least 250 days. (C) 2008 Elsevier B.V. All rights reserved
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据