JOURNAL OF MATERIALS RESEARCH
卷 24, 期 1, 页码 217-226出版社
MATERIALS RESEARCH SOC
DOI: 10.1557/JMR.2009.0010
关键词
-
资金
- Hungarian TeT Foundation (KPI) [F-47/2006]
- Hungarian Scientific Research Fund [K67692, K71594]
- Hungarian Academy of Sciences
Ultrafine-grained samples were produced front a Ni nanopowder by hot isostatic pressing (HIP) and spark plasma sintering (SPS). The microstructure and mechanical behavior of the two specimens were compared. The grain coarsen in observed during the SPS procedure was moderated due to a reduced temperature and time of consolidation compared with HIP processing. The smaller grain-size and higher nickel-oxide content in the SPS-processed sample resulted in a higher yield strength. Compression experiments showed that the specimen produced by SPS reached a maximal flow stress at a small strain, which was followed by a long steady-state softening while the HIP-processed sample hardened until failure. It was revealed that the softening of the SPS-processed sample resulted front microcracking along the grain boundaries.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据