The sol-gel autocombustion method has been used to synthesize the Ce-Zn substituted with composition Sr2-xCexNi2Fe28-yZnyO46 (x=0.02, 0.04, 0.06, 0.08, 0.010 and y=0.1, 0.2, 0.3, 0.4, 0.5) X-type hexagonal ferrites. The XRD analysis confirms the single phase of the material. The variation in lattice parameters can be observed with addition of Ce-Zn dopant. The ferrites substituted with Ce-Zn contents have low value of grain size than the unsubstituted ferrites. The crystallite size measured from TEM and HRTEM analysis was found in the range of 40-45 nm which is in good agreement with the theoretically measured by Scherer formula. The room temperature electrical resistivity lies in the range of similar to 10(9) Omega-cm, so the investigated sample can be considered good material for reducing the eddy current losses. The enhancement in magnetic properties (saturation magnetization, retentivity and coercivity) has been observed with the substitution of Ce-Zn contents in pure ferrites. The increment in resistivity and magnetic properties with the substitution of Ce-Zn dopant makes it important candidate to be used in the formation of multilayer chip inductors (MLCIs). The maximum reflection loss of -23.4 dB at 12.858 GHz is obtained by Ce-Zn doped ferrites and attenuation constant agrees well with the reflection loss. The microwave absorption properties of this substituted material reflect its applications in super high frequency (SHF) devices. (C) 2014 Elsevier B.V. All rights reserved,
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据