期刊
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
卷 371, 期 -, 页码 14-19出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jmmm.2014.07.007
关键词
Y-type hexaferrite (Co2Y); Sol-gel auto combustion; X-ray analyses; Magnetic properties
资金
- Iranian Nanotechnology Initiative Council [45519]
In this study, Mg and Ni substituted Y-Type hexaferrite particles with narrow size distribution have been prepared by using a sol-gel auto combustion method. The effects on structural, microstructure and magnetic properties have been investigated by substituting Mg2+ and Ni2+ at Co2+ sites. XRD patterns Showed that Y-type hexaferrite phase formation has not been affected by substituting magnesium and nickel with cobalt in the range of 0.0 <= x <= 0.75. Various parameters such as lattice constants, cell volume and crystallite size have been calculated based on XRD data The morphology and size distribution of the particles have been studied using high resolution held emission scanning electron microscopy (FESEM). It was also understood that the average crystallite size of particles increased from 45 to 63 nm with an increase of x content at CO2Y compound. Magnetic properties were determined using a vibrating sample magnetometer (VSM). The magnetic results revealed that by increasing the Mg and Ni in octahedral and tetrahedral sites, the coercivity was also increased from 949 to 1066 Oe, whereas saturation magnetization and Remnant magnetization were decreased from 47.98 to 40.78 emu/g and 23.05 to 20.99 emu/g, respectively. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据