This paper describes the fabrication of CoFe2O4 thick films using the tape casting method from nonaqueous slurry. CoFe2O4 particles with average size of similar to 800 nm were prepared by the solid-state reaction method. Sediment volumes and viscosity were tested to study the effects of dispersant in reducing aggregations in slurry. Slurry with 0.25 wt% dispersant amounts and 41.3 wt% solid content showed the optimal stability and rheological properties. A tape velocity of 8 cm/s was used in this study considering the non-Newtonian flow behavior at low shear rate. CoFe2O4 ceramic films sintered at 1150 degrees C for 2 h have dense structure (relative density of 94%) and exhibited ferromagnetic properties with in-plane saturation magnetization of similar to 324 emu/cm(3). (C) 2012 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据