JOURNAL OF HAZARDOUS MATERIALS
卷 157, 期 2-3, 页码 496-502出版社
ELSEVIER
DOI: 10.1016/j.jhazmat.2008.01.009
关键词
nickel oxide; microwave-enhance catalytic degradation (MECD); 4-chlorophenol
资金
- National Science Council of the Republic of China [NSC 95-2113-M-014-003, NSC M95-2113-M-026-001]
Microwave-enhance catalytic degradation (MECD) of 4-chlorophenol (4-CP) using nickel oxide was studied. A mix-valenced nickel oxide was obtained from nickel nitrate aqueous solution through a precipitation with sodium hydroxide and an oxidation by sodium hypochlorite (assigned as PO). Then, the as-prepared PO was irradiated under microwave irradiation to fabricate a high active mix-valenced nickel oxide (assigned as POM). Further, pure nanosized nickel oxide was obtained from the POM by calcination at 300, 400 and 500 degrees C (labeled as C300, C400 and C500, respectively). They were characterized by X-ray (XRD), infrared spectroscopy (IR) and temperature-programmed reduction (TPR). Their catalytic activities towards the degradation of 4-CP on the efficiency of the degradation were further investigated under continuous bubbling of air through the liquid-phase and quantitative evaluation by high pressure liquid chromatography (HPLC). Also, the effects of temperature, pH and kinds of catalysts on the efficiency of the degradation have been investigated. The results showed that the 4-CP was degraded completely by MECD method within 20 min under pH 7, T = 40 degrees C and C = 200 g dm(-3) over POM catalyst. The relative activity was affected significantly with the oxidation state of nickel. (C) 2008 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据