期刊
OPTICAL MATERIALS
卷 47, 期 -, 页码 219-224出版社
ELSEVIER
DOI: 10.1016/j.optmat.2015.04.067
关键词
Titanium nitride; Nanorod arrays; Surface enhanced Raman scattering
资金
- Shanghai Science and Technology Committee [12nm0504700]
- National Nature Science Foundation of China [51272066]
- Nature Science Foundation of Hebei Provincial [E2013209183]
TiN nanorod arrays (NRs) were prepared using a hydrothermal process followed by nitridation in ammonia atmosphere. The fabricated TiN NRs were characterized by UV-vis spectroscopy, X-ray diffraction analysis (XRD), scanning electron microscopy (SEM) and Transmission electron microscopy (TEM). The Surface-enhanced Raman scattering (SERS) activity of these substrates was evaluated by using Rhodamine (R6G) and crystal violet (CV) as the probe molecules. Results showed that TIN NRs prepared at 900 degrees C exhibited the strongest Raman enhancement performance. The average sizes of the TiN NRs were 57 nm. The TIN NRs had an absorption peak around 524 nm, which related to surface Plasmon resonance. Compared to the CV molecules, the R6G molecules can obtain a higher enhancement in our substrate. The enhancement factor ((8.9 +/- 0.2) x 10(3)) and the R6G detection limit (10(-6)M) were achieved. The results showed that the TiN NRs are a kind of promising materials as SERS sensor. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据