期刊
JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART A
卷 87A, 期 3, 页码 643-655出版社
WILEY
DOI: 10.1002/jbm.a.31703
关键词
calcium phosphate cement; gelatin; microsphere; degradation
资金
- Dutch Technology Foundation STW [NGT 6205]
For tissue engineered bone constructs, calcium phosphate cement (CPC) has a high potential as scaffold material because of its biocompatibility and osteoconductivity. However, in vivo resorption and tissue ingrowth is slow. To address these issues, microspheres can be incorporated into the cement, which will create macroporosity after in situ degradation. The goal of this study was to investigate the handling properties and degradation characteristics of CPC containing gelatin microspheres. Setting time and injectability were determined and an in vitro degradation study was performed. Samples were assayed on mass, compression strength, E-modulus, and morphology. A supplementary degradation test with gelatin microspheres was performed to investigate the influence of physical conditions inside the cement on microsphere stability. The gelatin microsphere CPCs were easy to inject and showed initial setting times of less than 3 min. After 12-weeks in vitro degradation no increase in macroporosity was observed, which was supported by the small mass loss and stabilizing mechanical strength. Even a clear densification of the composite was observed. Explanations for the lack of macroporosity were recrystallization of the cement onto or inside the gelatin spheres and a delayed degradation of gelatin microspheres inside the scaffold. The supplementary degradation test showed that the pH is a factor in the delayed gelatin microsphere degradation. Also differences in degradation rate between types of gelatin were observed. Overall, the introduction of gelatin microspheres into CPC renders composites with good handling properties, though the degradation characteristics should be further investigated to generate a macroporous scaffold. (C) 2008 Wiley Periodicals, Inc. J Biomed Mater Res 87A: 643-655, 2008
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据