JOURNAL OF APPLIED POLYMER SCIENCE
卷 131, 期 21, 页码 -出版社
WILEY
DOI: 10.1002/app.40966
关键词
composites; crosslinking; electrospinning; nanostructured polymers
资金
- U.S. National Science Foundation [CHE-1012279]
- Direct For Mathematical & Physical Scien
- Division Of Chemistry [1012279] Funding Source: National Science Foundation
Small diameter nanofibers of silica and silica/polymer are produced by electrospinning silica/polyvinylpyrrolidone (SiO2/PVP) mixtures composed of silica nanoparticles dispersed in polyvinylpyrrolidone solutions. By controlling various parameters, 380+/-100 nm diameter composite nanofibers were obtained with a high silica concentration (57.14%). When the polymer concentration was low, beads-on-a-string morphology resulted. Nanofiber morphology was affected by applied voltage and relative humidity. Tip-to-collector distance did not affect the nanofiber diameter or morphology, but it did affect the area and thickness of the mat. Heat treatment of the composite nanofibers at 200 degrees C crosslinked the polymer yielding solvent-resistant composite nanofibers, while heating at 465 degrees C calcined and selectively removed the polymer from the composite. Crosslinking did not change the nanofiber diameter, while calcined nanofibers decreased in diameter (300+/-90 nm) and increased in surface area to volume ratio. Nanofibers were characterized by scanning electron microscopy (SEM) and thermogravimetric analysis (TGA). (C) 2014 Wiley Periodicals, Inc.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据