期刊
JOURNAL OF APPLIED POLYMER SCIENCE
卷 129, 期 5, 页码 2806-2812出版社
WILEY-BLACKWELL
DOI: 10.1002/app.38839
关键词
coatings; crosslinking; membranes; separation techniques
资金
- National High Technology Research and Development Program (863 Program of China) [2012AA03A602]
- National Department Public Benefit Research Foundation [201210217]
Poly(N,N-dimethylaminoethyl methacrylate) (PDMAEMA) can be crosslinked by interfacial polymerization to develop a positively charged dense network structure. According to this mechanism, a positively charged hollow-fiber composite nanofiltration (NF) membrane was prepared by quaternization to achieve a crosslinked PDMAEMA gel layer on the outer surface of polysulfone hollow-fiber ultrafiltration (UF) membranes with a PDMAEMA aqueous solution as a coating solution and p-xylylene dichloride as an agent. The preparation conditions, including the PDMAEMA concentration, content of additive in the coating solution, catalyzer, alkali, crosslinking temperature, and hollow-fiber substrate membrane, were studied. Fourier transform infrared spectroscopy and scanning electron microscopy were used to characterize the structure of the membranes. This membrane had a rejection to inorganic salts in aqueous solution. The rejection of MgSO4 (2 g/L aqueous solution at 0.7 MPa and 25 degrees C) was above 98%, and the flux was about 19.5 L m-2 h-1. Moreover, the composite NF membranes showed good stability in the water-phase filtration process. (c) 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据