polylactide; methyl methacrylate-butadiene-styrene; blends; toughening
资金
- Science and Technology Bureau of Jilin Province of China [20090320]
- Ministry of Science and Technology of China [2009GJB10042]
- Chinese Science Academy (Changchun Branch) [2009SYHZ0028]
Brittle polylactide (PLA) was toughened by introducing 5-25 wt % of methyl methacrylatebutadienestyrene (MBS) copolymer. PLA/MBS blends were characterized by dynamic mechanical analysis (DMA), differential scanning calorimetry (DSC), dynamic rheometer, mechanical testing, scanning electron microscopy, and transmission electron microscope. From the result of DSC, MBS could act as an effective heterogeneous nucleation agent for PLA and significantly improved the degree of crystallinity of PLA. DMA results showed a single high temperature peak of Tg between that of pure PLA and that of the shell composition of the MBS, which suggested that PLA and the shell of MBS were compatible. With an increase of MBS content, the tensile strength of the blends decreased; however, the elongation at break and impact strength increased significantly which indicated the toughening effects of the MBS on PLA. It was found that the PLA matrix showed large plastic deformation (shear yielding) in the blend subjected the impact tests, which was an important energy-dissipation process and led to a toughened polymer blend. MBS could act as impact modifier of PLA. Rheological investigation demonstrated that there was a significantly dependence of viscosity on composition. When the MBS content increased, the viscosity began to increase. (C) 2012 Wiley Periodicals, Inc. J Appl Polym Sci, 2012
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据