期刊
JOURNAL OF APPLIED PHYSICS
卷 107, 期 12, 页码 -出版社
AMER INST PHYSICS
DOI: 10.1063/1.3437068
关键词
-
资金
- NIH [P41-EB21820]
- ONR [N00014-09-1-01456, N-00014-07-C-0858]
The dielectric and piezoelectric properties of Pb(Mg1/3Nb2/3)O-3-PbTiO3 (PMN-PT) and Pb(In1/2Nb1/2)O-3-Pb(Mg1/3Nb2/3)O-3-PbTiO3 (PIN-PMN-PT) ferroelectric single crystals were investigated as a function of thickness/scale in monolithic and piezoelectric/polymer 1-3 composites. For the case of PMN-PT single crystals, the dielectric (epsilon(T)(33)/epsilon(0)) and electromechanical properties (k(33)) were found to significantly decrease with decreasing thickness (500-40 mu m), while minimal thickness dependency was observed for PIN-PMN-PT single crystals. Temperature dependent dielectric behavior of the crystals suggested that the observed thickness dependence in PMN-PT was strongly related to their relatively large domain size (>10-20 mu m). As anticipated, 1-3 composite comprised of PIN-PMN-PT crystals exhibited superior properties to that of PMN-PT composite at high frequencies (>20 MHz). However, the observed couplings, being on the order of 80%, were disappointedly low when compared to their monolithic counterparts, the result of surface damage introduced during the dicing process, as evidenced by the broadened [002] peaks in the x-ray diffraction pattern. (c) 2010 American Institute of Physics. [doi:10.1063/1.3437068]
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据