期刊
JOURNAL OF APPLIED ELECTROCHEMISTRY
卷 43, 期 6, 页码 611-617出版社
SPRINGER
DOI: 10.1007/s10800-013-0542-5
关键词
Iron phosphate; LiFePO4/C composite; Chemical lithiation; Size-controllable; Electrochemical performance
资金
- Natural Science Foundation of China [11275121, 21241002]
- Science and Technology Committee of Shanghai [11DZ110020, 10ZR1411300]
- Shanghai Leading Academic Disciplines Project [S30109]
Chemical lithiation of amorphous FePO4 with LiI in acetonitrile is performed to form amorphous LiFePO4. The amorphous FePO4 center dot 2H(2)O precursor is synthesized by co-precipitation method from equimolar aqueous solutions of FeSO4 center dot 7H(2)O and NH4H2PO4, using H2O2 (hydrogen peroxide) as the oxidizing agent. The nanocrystalline LiFePO4/C is obtained by annealing the amorphous LiFePO4 and in situ carbon coating with sucrose in a reducing atmosphere. The particle size of FePO4 center dot 2H(2)O precursor decreases with increasing reaction temperature. The final LiFePO4/C products completely maintain the shape and size of the precursor even after annealing at 700 A degrees C for 2 h. The excellent electrochemical properties of these nanocrystalline LiFePO4/C composites suggest that to decrease the particle size of LiFePO4 is very effective in enhancing the rate capability and cycle performance. The specific discharge capacities of LiFePO4/C obtained from the FePO4 center dot 2H(2)O precursor synthesized at 75 A degrees C are 151.8 and 133.5 mAh g(-1) at 0.1 and 1 C rates, with a low capacity fading of about 0.075 % per cycle over 50 cycles at 0.5 C rate.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据