Field electron emission enhancement of graphenated MWCNTs emitters following their decoration with Au nanoparticles by a pulsed laser ablation process

A plasma-enhanced chemical vapor deposition (PECVD) process was adapted to alter the growth of multiwall carbon nanotubes (MWCNTs) so that graphene sheets grow out of their tips. Gold nanoparticle (Au-NP) decoration of graphenated MWCNTs (g-MWCNTs) was obtained by subsequent decoration by a pulsed laser deposition (PLD) process. By varying the number of laser ablation pulses (NLp) in the PLD process, we were able to control the size of the gold nanoparticles and the surface coverage of the decorated g-MWCNTs. The presence of Au-NPs, preferentially located at the tip of the g-MWCNTs emitters, is shown to significantly improve the field electron emission (FEE) properties of the global g-MWCNT/Au-NP nanohybrid films. Indeed, the electric field needed to extract a current density of 0.1 mu A cm(-2) from the g-MWCNT/ Au-NP films was decreased from 2.68 V mu m(-1) to a value as low as 0.96 V mu m(-1). On the other hand, UV photoelectron spectroscopy (UPS) characterization revealed a decrease in the global work function of the Au-decorated g-MWCNT nanohybrids compared to that of bare gMWCNT emitters. Surprisingly, the work function of g-MWCNT was found to decrease from 4.9 to 4.7 eV with the addition of Au-NPs-a value lower than the work function of both materials worth 5.2 and 4.9 eV for gold and g-MWCNT, respectively. Our results show that the NLp dependence of the FEE characteristics of the g-MWCNT/Au-NP emitters correlates well with their work function changes. Fowler-Nordheim-theory-based calculations suggest that the significant FEE enhancement of the emitters is also caused by the Au-NPs acting as nanoscale electric field enhancers.