JOURNAL OF ANALYTICAL AND APPLIED PYROLYSIS
卷 83, 期 2, 页码 185-189出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jaap.2008.08.007
关键词
WEEE; PCB; Pyrolysis; Recycling; Mechanical strength
资金
- National High Technology Research and Development Key Program of China [2006AA06Z366]
This paper is part of a project which Studies pyrolysis as an alternative for recycling printed Circuit board (PCB); the sample (2.0 cm x 2.0 cm) was pyrolyzed under nitrogen atmosphere, at 300, 400, 500, 600 and 700 degrees C in a tubular type Oven, Maintaining 30 min, and during the pyrolysis process the organic part is decomposed to pyro-oils and pyro-gases, which can be used as fuels or chemical material resources: the solid residues of about 75-80 wt%, liquid yields of similar to 9.0 wt.% and gas yields of 12-14 wt.%. No significant influence of temperature was observed over 500 degrees C, however, there was certainly influence under 500 degrees C in both volatile Substance. The pyro-oils have fairly high gross Calorific Values (similar to 30 kJ/kg), mainly with aromatic and with oxygenated compounds. The pyro-gas is very rich in CO. CO2, H-2, CH4 and in small part of O-2; after being purged it can be combusted for the pyrolysis self-sustain. The tensile strength decreases about 35% at 773 K, while the impact and tear strength increases above 773 K, and then decreases along with the temperature increase. The strength changes can offer guidance for used as a replacement for virgin fibres in SMC manufacture. The residues are better laminated can be easily liberated for metals recovery. (c) 2008 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据