The temporal evolution of the Al-3(ErZr) precipitates is investigated in Al-0.04Er-0.04Zr and Al-0.04 Er-0.08Zr alloys during aging at elevated temperature of 450 and 500 degrees C. The results show that the coarsening behavior of the precipitates in both alloys is similar, due to the core-shell structure with Zr segregated in the shell of the Al-3(ErZr) precipitates. With the increase of the amount of Zr addition, the misfit between the precipitate and the Al matrix decreases, consequently the coherency transition size of the precipitates in Al-0.04Er-0.08Zr is larger than that of Al-0.04Er-0.04Zr. After aging at 500 degrees C for 100 h, some of the precipitates in Al-0.04Er-0.08Zr transform to D0(23) structure due to the high Zr/Er ratio, while the precipitates in Al-0.04Er-0.04Zr keep the L1(2) structure. (C) 2013 Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据