Silver nanoparticles prepared by chemical reduction-protection method, and their application in electrically conductive silver nanopaste

Ag nanoparticles were prepared in a water-phase system with a mixture of silver-ammonia complex, sodium borohydride, and lauric acid according to molar feed ratio of approximately 6:3:1. The mechanism of preparation and separation by chemical reduction-protection method was explored. The as-synthesized Ag nanoparticles were characterized by transmission electron microscopy (TEM), X-ray diffraction (XRD) and UV-vis spectroscopy, respectively. It was found that the size of high purity Ag particles was ranging from 30 to 50 nm with slight agglomeration. In addition, the as-synthesized wet Ag nanoparticles were dispersed stably in organic vehicle to formulate electrically conductive nanopaste. Upon direct-written and sintered, the array pattern of the nanopaste with the resolution of about 30 mu m was achieved with the electrical resistivity in the order of magnitude of 10(-5) Omega cm. (C) 2010 Elsevier B.V. All rights reserved.