JOURNAL OF ALLOYS AND COMPOUNDS
卷 490, 期 1-2, 页码 637-641出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2009.10.124
关键词
Bismuth ferrite; Magnetic property; Dielectric property; Lanthanum doping; Hydrothermal
资金
- Australian Research Council [DP0987190]
- University of Wollongong
- Australian Research Council [DP0987190] Funding Source: Australian Research Council
Multiferroic Bi1-xLaxFeO3 (x=0.0, 0.1, 0.2, and 0.3) micro-particles were successfully synthesized by a hydrothermal technique. All the samples were phase pure crystallizing in a perovskite structure with a space group of R3c. XRD refinement revealed that the lattice parameters increased along with increase of La content, while the Fe-O octahedra became more distorted. It was found that the morphologies of as-obtained micron-sized particles turned from spheroidal to octahedral according to different doping levels. The dielectric constant of Bi1-xLaxFeO3 sample increased after La doping, and reached the largest value for the sample of x = 0.2, both in low and high frequency range at room temperature. All the as-prepared samples exhibited magnetic moments starting above room temperature. It was found that the magnetic moment was significantly enhanced from 0.264 emu/g of BiFeO3 to 0.658 emu/g of Bi0.9La0.1FeO3 in a field of 3T at 77K. Both enhancements of ferromagnetic and dielectric properties possibly attribute to the changes of lattice parameters and Fe-O bond lengths caused by lanthanum substitution. (C) 2009 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据