期刊
JOURNAL OF ALLOYS AND COMPOUNDS
卷 482, 期 1-2, 页码 240-245出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2009.03.169
关键词
Chemical synthesis; Oxides; Nanostructures; Optical properties
资金
- National Natural Science Foundation of China [50701024]
- National Key Project of Fundamental Research [2007CB936300]
- China Postdoctoral Science Foundation [20080430164, 200801366]
- Jiangsu Postdoctoral Science Foundation [0801040B]
Cu2O nanowires were successfully fabricated by a simple liquid reaction in the presence of amphiphilic triblock copolymer (P123). The concentration of copolymer and aging time drastically changed the morphology of Cu2O samples. XPS results show that tiny amount of CuO as well as some absorbed O-2 molecules existed on the surface of the Cu2O nanowires. Thermal analysis shows that the triblock copolymer owns a higher decomposition temperature (similar to 645 degrees C) than that of pervious research results and this may be the result of strong interaction between P123 and Cu2O. The band gap of Cu2O nanowires was estimated about 2.23 eV and shifting of the band gap with decreasing of the particle size could also be found. The photoluminance property study reveals that the intrinsic emission peak Of Cu2O nanowires can be observed at 546 nm under the excitation wavelength of 400 nm (Xe lamp was used as the excitation light source). (C) 2009 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据