Fabrication and thermoelectric properties of Ca3Co4O9/Ag composites

Ca3Co4O9/Ag thermoelectric composites were fabricated by hot-pressing the composite powders prepared by a solution chemical process. No second phases or unwanted reaction phase were found in Ca3Co4O9/Ag composites. SEM micrographs revealed that composites exhibited a textured structure and the Ag particles with similar to 0.1 to several mu m in size distributed at Ca3Co4O9 grain boundaries. Addition of Ag particles has a strong influence on densification and texture development in Ca3Co4O9/Ag composites. By adding Ag particles, the Seebeck coefficient (S) and electrical resistivity (rho) of composites decrease simultaneously. The power factor (P) of Ca3Co4O9/Ag is found to be improved due to the remarkable reduction in rho. However, the value decreases when the Ag content is above 7.5 vol.% because the value of S is obviously deteriorated by the presence of large amounts of Ag particles. (C) 2007 Elsevier B.V. All rights reserved.