Epitaxial BiFeO3 (BFO) thin films with striped- and single-domain structures have been grown on SrTiO3 (STO) (103) and (113) substrates by radiofrequency planar magnetron sputtering. The domain structure of BFO was controlled by the orientation of the STO substrate. Piezoelectric force microscopy revealed that BFO thin films on STO (103) and STO (113) had a striped-domain structure with 71 domain walls running along (010)s-ro, and a single-domain structure, respectively. To confirm the photovoltaic property, rectangular Pt electrodes with widths of 150-200 pm were deposited on BFO surfaces with interelectrodes distances of 200-250 mu m. I-V characteristics were measured under an illumination of a collimated violet laser (lambda = 405 nm) with a power density of 380 W/cm(2). In the striped-domain-structure BFO film with Pt electrodes fabricated along domain walls, above-band-gap open-circuit voltage (V-OC) of 29V was observed. In addition, single-domain-structured BFO thin film with Pt electrodes fabricated along (110) also showed above-band-gap V-oc of 26V despite the absence of domain walls. It is considered that these large 1/00 values originated from the photovoltaic effect not at the domain walls but in bulk BFO. (C) 2014 The Japan Society of Applied Physics
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据