INTERNATIONAL JOURNAL OF FATIGUE
卷 63, 期 -, 页码 25-35出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ijfatigue.2014.01.002
关键词
Composites; Multiaxial fatigue; Crack initiation; Crack propagation; Damage modes
The matrix-dominated behaviour of unidirectional composite laminae subjected to multiaxial fatigue loading was extensively investigated. Tubular specimens with three different lay-up ([90(n)], [0(F)/90(U,3)] and [0(F)/90(U,3)/0(F)]) were tested under combined tension/torsion loadings. Attention was focused on the initiation and propagation of cracks in the 90 degrees layers, and fatigue data are presented in terms of S-N curves (for crack initiation) and Paris-like curves (for crack propagation) under several biaxiality ratios. Damage onset and evolution have been found to be strongly affected by the multiaxial loading condition, showing a particularly detrimental effect of the shear stress component. SEM investigations on the fracture surfaces confirmed a strong dependence also of the microscopic damage modes on the local multiaxial stress state. (C) 2014 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据