MATERIALS TRANSACTIONS
卷 56, 期 7, 页码 952-956出版社
JAPAN INST METALS & MATERIALS
DOI: 10.2320/matertrans.MH201415
关键词
microtension testing; magnesium alloys; plastic deformation; slip; twinning
资金
- Japan Society for the Promotion of Science (JSPS) [21360343]
- Ministry of Education, Culture, Sports, Science and Technology of Japan [26109718]
- Grants-in-Aid for Scientific Research [26109718, 21360343] Funding Source: KAKEN
Microtension tests were performed on single crystals with different crystallographic orientations, which were prepared using an 18R-type long-period stacking ordered (LPSO) structure in a directionally solidified Mg85Zn6Y9 alloy. Anisotropic plasticity was observed for the LPSO phase specimens. Cleavage cracking occurred on the prismatic planes in a crystal with its loading direction parallel to the basal plane. The cleavage stress for the prismatic plane was determined to be approximately 460 MPa. A crystal that was oriented favorably for gliding on the basal plane exhibited a critical resolved shear stress of approximately 9.4 MPa. When a crystal was loaded along [0001], a sudden load drop was observed at a stress of approximately 250 MPa in the initial linear region of the stress-strain relation. Transmission electron microscopy results after the load drop showed that the deformation microstructure contained a twin-like boundary with a rotation axis along [11 (2) over bar0].
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据