Thickness Dependent Magnetic Anisotropy of Ultrathin LCMO Epitaxial Thin Films

The magnetic properties of La(0.7)Ca(0.3)MnO(3) (LCMO) manganite thin films were studied with magnetometry and ferromagnetic resonance as a function of film thickness. They maintain the colossal magnetoresistance behavior with a pronounced metal-insulator transition around 150-200 K, except for the very thinnest films studied (3 nm). Nevertheless, LCMO films as thin as 3 mm remain ferromagnetic, without a decrease in saturation magnetization, indicating an absence of dead-layers, although below approximately 6 nm the films remain insulating at low temperature. Magnetization hysteresis loops reveal that the magnetic easy axes lie in the plane of the film for thicknesses in the range of 4-15 nm. Ferromagnetic resonance studies confirm that the easy axes are in-plane, and find a biaxial symmetry in-plane with two, perpendicular easy axes. The directions of the easy axes with respect to the crystallographic directions of the cubic SrTiO(3) substrate differ by 45 deg in 4- and 15-nm-thick LCMO films.