Effect of Ag/TiO2 core/shell nanostructures on the photocatalytic activity of the TiO2/rGO nanocomposite material

作者

Evgeniya Seliverstova¹ , Timur Serikov¹ , Aigyl Sadykova¹ , Niyazbek Ibrayev¹

1. Institute of Molecular Nanophotonics, Buketov Karaganda University

会议/活动

8th Asian Symposium on Advanced Materials (ASAM-8), July 2023 (Novisibirsk, Russian Federation)

海报摘要

The effect of Ag/TiO2 core/shell plasmonic nanostructures on the photocatalytic activity of a nanocomposite material based on TiO2 and reduced graphene oxide (rGO) was studied. The nanocomposite was obtained by hydrothermal synthesis. Ag/TiO2 nanostructures are consisted of Ag NPs with an average diameter of 26 nm and a TiO2 shell of 10 nm thick, were added to the prepared nanocomposite at concentrations of 0.1, 0.3 and 0.5 wt%. Measurements have shown that the presence of Ag/TiO2 nanostructures leads to the increase in photocurrent values in 2.8 times compared to films without plasmon NPs. It was found that nanocomposite films doped with Ag/TiO2 have a lower values of resistance to charge carrier transport, as well as resistance associated with recombination processes. In addition the lifetime of charge carriers was increased in the presence of plasmon NPs.

关键词

Titanium oxide, Reduced graphene oxide, Core/shell nanostructure, Nanocomposite, Photocathalytic properties, Impedance

研究领域

Physics, Material Sciences, Nanoengineering

参考文献

暂无数据

基金

1. This research is funded by the Science Committee of the Ministry of Science and Higher Education of the Republic of Kazakhstan (No. AP14871956)

补充材料

暂无数据

附加信息

利益冲突

No competing interests were disclosed.

数据可用性声明

The datasets generated during and / or analyzed during the current study are available from the corresponding author on reasonable request.

知识共享许可协议

Copyright © 2023 Seliverstova et al. This is an open access work distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.